Phase Equilibria in the Cu2Se−SnSe−CuSbSe2 System

Ismailova E., Mashadieva L., Bakhtiyarly I., Babanlı M.

Russian Journal of Inorganic Chemistry, vol.64, no.6, pp.801-809, 2019 (SCI-Expanded, Scopus) identifier

  • Nəşrin Növü: Article / Article
  • Cild: 64 Say: 6
  • Nəşr tarixi: 2019
  • Doi nömrəsi: 10.1134/s0036023619060093
  • jurnalın adı: Russian Journal of Inorganic Chemistry
  • Jurnalın baxıldığı indekslər: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Səhifə sayı: pp.801-809
  • Açar sözlər: copper antimony selenides, liquidus surface, phase diagram, tin monoselenide
  • Açıq Arxiv Kolleksiyası: Məqalə
  • Adres: Bəli

Qısa məlumat

Phase equilibria in the Cu2Se−SnSe−CuSbSe2 system were studied by differential thermal and X-ray powder diffraction analyses. Alloys were obtained by alloying of the preliminarily synthesized and identified initial compounds in a vacuum with subsequent annealing at 650 K for 500 h. Characteristic plots describing this system were constructed, namely, the polythermal sections SnSe−Cu3SbSe3, Cu2Se−[A], and CuSbSe2−[B], where [A] and [B] are the alloys of the compositions (SnSe)0.5(CuSbSe2)0.5 and (Cu2Se)0.5(SnSe)0.5, respectively; the isothermal section of the phase diagram at 300 K; and the projection of the liquidus surface. It was shown that this system is a quasi-ternary section of the quaternary system Cu−Sn−Sn−Se and is characterized by invariant equilibria: a transient one and a eutectic one. Fields of primary crystallization of phases and the types and coordinates of in- and monovariant equilibria were found. Wide regions of solid solutions based on SnSe and CuSbSe2 were revealed.