Structural peculiarities and photoluminescence of ZnGa2Se4 compound

Tagiyev B., Tagiyev O., Kerimova T., Guseynov G., Əsədullayeva S.

Physica B: Condensed Matter, vol.404, no.23-24, pp.4953-4955, 2009 (SCI-Expanded) identifier

  • Nəşrin Növü: Article / Article
  • Cild: 404 Say: 23-24
  • Nəşr tarixi: 2009
  • Doi nömrəsi: 10.1016/j.physb.2009.08.276
  • jurnalın adı: Physica B: Condensed Matter
  • Jurnalın baxıldığı indekslər: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Səhifə sayı: pp.4953-4955
  • Açar sözlər: Crystal structure, Europium, Manganese, Photoluminescence
  • Açıq Arxiv Kolleksiyası: Məqalə
  • Adres: Bəli

Qısa məlumat

In ZnGa2Se4 and ZnGa2Se4:Eu crystals photoluminescence (PL) at T=77-230 K has been investigated. In the PL spectrum of ZnGa2Se4 maximum was found at 591 nm, ZnGa2Se4:Eu spectrum maxima at 566, 591 and 646 nm, but in ZnGa2Se4:Mn spectrum maxima were found at 626 and 641 nm. Most probably the introduction of Eu and Mn ions into ZnGa2Se4 decreases the structural defects. © 2009 Elsevier B.V. All rights reserved.