Phase relations in the SnSe2-Er2Se3 system

Bagieva M., Aliev I., Babanlı M.

Inorganic Materials, vol.39, no.9, pp.927-930, 2003 (SCI-Expanded, Scopus) identifier

  • Nəşrin Növü: Article / Article
  • Cild: 39 Say: 9
  • Nəşr tarixi: 2003
  • Doi nömrəsi: 10.1023/a:1025501103988
  • jurnalın adı: Inorganic Materials
  • Jurnalın baxıldığı indekslər: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Səhifə sayı: pp.927-930
  • Açıq Arxiv Kolleksiyası: Məqalə
  • Adres: Bəli

Qısa məlumat

The phase diagram of the SnSe2-Er2Se3 system is studied using differential thermal analysis, x-ray diffraction, microstructural analysis, and microhardness and density measurements. The SnSe2-Er2Se3 system is pseudobinary and contains two eutectics and two intermediate phases, Er2Sn 3Se9 and Er2SnSe5. At room temperature, the SnSe2-based solid solution extends to ≃4.5 mol % Er2Se3, and the SnSe2 solubility in Er 2Se3 is ≃2 mol %.